Sheets and profile.Good impact strengthHigh toughness
Plain or coextruded with high drawRatios for refrigeration, sanitaryAutomotive,Packaging, housholding (profiles)
Packaged product should be protected from the atmosferic agents and stored out of direct sunlightNB: No Break/M: Matt - Digit following letter/M indicates increasing values of mattness
Properties
Test Condition
Test Methods
Units
General
Density
ISO 1183
g/cm3
1.04
Water Absorption
ASTM D 570
%
0.3
Rheological
Melt Flow Rate (MFR)
ISO 1133
g/10min
5
Mechanical
Tensile Strength
50 mm/min
ASTM D 638
MPa
35
Strain at break
45
Flexural Strength
2 mm/min
ASTM D 790
68
Flexural Modulus
2300
Izod Impact Strength Notched
+23°C - thickness 3.2 mm
ISO 180/4A
J/m
280
0°C - thickness 3.2 mm
190
- 20°C - thickness 3.2 mm
150
- 40°C - thickness 3.2 mm
125
+23°C - thickness 4 mm
ISO 180/1A
kJ/m²
20
- 40°C - thickness 4 mm
10
Charpy Impact Strength, Notched
+23°C
DIN 53453
16
Unnotched
NB
- 40°C
Rockwell Hardness
scale R
ISO 2039/2
R110
Thermal
Vicat Softening Tempreture
10 N - 120°C/h
ISO 306/A120
ºC
108
50 N - 120°C/h
ISO 306/B120
104
Deflection temp. under load (annealed)
1.8 MPa - 120°C/h
ASTM D 648
Ceofficient of linear thermal expansion
ASTM D 696
10 -5/ºC
9
Thermal Conductivity
ASTM C 177
W/(Km)
0.17
Moulding Shrinkage
ISO 294.4
0.4-0.6
Flammability
Flame behavior
thickness 1.5 mm
UL 94
class
HB
Glow wire test
thickness 3 mm
IEC 60695-2-1
650
Electrical
Surface resistivity
dry
IEC 60093
ohm
10+14
Volume resistivity
ohm*cm
10+15
Dielectric strength
IEC 60243
kV/mm
30
Dielectric constant (relative permittivity)
1000 Hz - dry
IEC 60250
3.1
Dissipation factor
15*10-³